Waterborne High Gloss Hydroxy Functional Polyacrylic Dispersion Acrylic Resin For Metal Coatings

Product Categories

Solvent Based Solid Acrylic Resin [15]
Waterborne Acrylic Resin [21]
Wax Additive [16]
Hydroxyl Acrylic Resin [26]
2K Epoxy Resin and Curing Agents [16]
Saturated Polyester Resin [5]
Alkyd Resin [5]
1K Industrial Coating Resins [5]
Water Based Polyurethane Dispersions [6]

Xiamen WangQin Chemical Technology Co., Ltd.

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Waterborne High Gloss Hydroxy Functional Polyacrylic Dispersion Acrylic Resin For Metal Coatings

Name: Waterborne High Gloss Hydroxy Functional Polyacrylic Dispersion Acrylic Resin For Metal Coatings
Brand: WeiLi Resin®
Price: 1 USD

Quality Waterborne High Gloss Hydroxy Functional Polyacrylic Dispersion Acrylic Resin For Metal Coatings for sale

Brand Name : WeiLi Resin®

Model Number : WL-AD3953

Certification : ISO9001

Place of Origin : China

MOQ : 5000kg

Price : Negotiable

Payment Terms : ,L/C,T/T

Supply Ability : 500t/month

Product Name : Waterborne Hydroxyl Acrylic Resin

Non-Volatile content（%） : 45±1

Viscosity（m Pa · s） : 500~4500

PH : 7.5~8.5

Hydroxyl content (reference value, %) : 3.3%

Pencil hardness (baking) : H

Contact Now

WL-AD3953 is an aqueous hydroxy-functional polyacrylic dispersion specifically formulated for coating applications on metal substrates, including basecoats, topcoats, and clearcoats. This hydroxylated acrylic dispersion serves as a direct replacement for Bayhydrol A2470 when used in combination with complementary resin systems from our product line.

Key characteristics include:

Crosslinking capability with aliphatic polyisocyanates to form high-gloss finishes
Flexible curing options: ambient temperature drying or accelerated curing at 80°C
Exceptional film properties:
- Balanced hardness and elasticity
- Superior resistance to solvents, water, and environmental exposure
Performance advantages:
- Rapid hardness development
- High threshold for bubble-free film formation
- Broad chemical resistance
- Excellent compatibility with solvent-borne isocyanate crosslinkers

The cured coating system demonstrates outstanding durability for industrial applications requiring both aesthetic appeal and long-term protection. Typical uses include automotive refinish, industrial maintenance coatings, and metal packaging finishes where regulatory-compliant, waterborne solutions are preferred.

Physical Property

Item	Value
Appearance	Milky white liquid
Non-Volatile content(%)	45±1
Viscosity(m Pa · s)	500~4500
PH	7.5~8.5
Hydroxyl content (reference value, %)	3.3

*This performance represents typical results only and is not considered a specification, subject to specific COA

The film parameters of WL-AD3953 reacting with a group of isocyanate curing agents are as follows:

Item	WL-AD3953/TPA-100 (BGA dilution)
Surface drying time(25℃/35% outdoor corridor In breeze)	30min
Surface drying time(14.5℃/60% outdoor corridor Under medium to high humidity conditions)	80min
Water resistance at room temperature	15 days
Pencil hardness (baking)	H
Bending resistance (mm)	<1
Impact (positive/negative cmkg)	50/30
Effective Validity period at 35℃	3h

‌Application Guidelines‌

When combining with solvent-based isocyanate curing agents:

‌Dilution Requirement‌: First dilute the dispersion to 60-70% concentration using suitable co-solvents (e.g., BGA, PGDA, or PMA+DBE blend at 1:2 ratio)
‌Mixing Protocol‌:
- Thoroughly blend main resin component and curing agent after combination
- Ideal mixing method: Use mechanical stirring equipment (pneumatic or electric stirrer)
‌Water Content Control‌:
- Limit water dilution: Recommended ≤5% of main resin component
- Absolute maximum: ≤10% of main resin component
  (Exceeding 10% causes gloss reduction)
‌Stability Precautions‌:
- Avoid resin participation in pigment grinding processes
- Grinding operations introduce multiple instability factors
- May compromise dispersion stability during color paste preparation
- Store:
  
  Packaging specifications: 20KG/200KG/1000KG plastic barrel
  
  Shelf life: 6 months
  
  Product transportation: Handle with care to avoid impact, damage and leakage.
  
  Product storage: The product should be stored in a sealed container to avoid freezing and high temperature. The
  
  recommended storage temperature is 5~35℃

Waterborne High Gloss Hydroxy Functional Polyacrylic Dispersion Acrylic Resin For Metal Coatings Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Xiamen WangQin Chemical Technology Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!